PRODUCTS FOR STAINLESS STEELS - CAST IRON
| Product GOLD |
Description |
Technical details |
Size (mm) |
| 310 |
JOINING STAINLESS STEELS
Highly alloyed , easy to weld stainless steel maintenance electrode.Cr-Ni-Mo with very low carbon , for welding 304, 304L, 347,316L, 318 stainless steels at service temperatures of –120°C to 350°C. |
Rm (Mpa) : 580
Re (Mpa) : 420
A5 (%) : 40 |
2.5
3.2
4.0 |
| 340 |
FOR HIGH TEMPERATURE APPLICATIONS
Electrode for fabrication and repair welding of high temperature equipments ( service temperature up to 1200°C). Used in chemical and petrochemical industries, for furnaces and heat treatment installations also used for welding of unknown or dissimilar steel types. |
Rm (Mpa) : 550
Re (Mpa) : 400
A5 (%) : 30 |
2.5
3.2 |
| 601 |
Highly alloyed , easy to weld stainless steel maintenance electrode., for welding 18/8 grade (304, 304L, 321,347) UGINOX 18-9 B,D,E M and similar stainless steels. |
Rm (Mpa) : 540
Re (Mpa) : 360
A5 (%) : 35 |
1.5
2.0
2.5
3.2
4.0 |
| 655 |
FOR DUPLEX/STAINLESS STEEL
Special electrode to welding of stainless and steel parts subject to high corrosion. Highest resistance to pitting and chloride containing solutions. Weld metal has high strength |
Rm (Mpa) : 700
Re (Mpa) : 520
A5 (%) : 25 |
2.5
3.2 |
| |
WELDING OF CAST IRON |
|
|
| 410 |
Electrode for cold repair welding of most different types of cast iron.
Use for welding and rebuilding of frames, gear box, machine and pump housings, engine blocks, casting defects, pulleys, compressors…
Weld metal composition :Ni > 95, Fe, Mn, C, Si |
Rm (Mpa) : 350
Hardness : 180 HB |
2.5
3.2 |
| 420 |
High strength Fe Ni Alloy electrode for cold welding of different Cast irons such as grey cast iron nodular cast iron and for joining cast iron to steel. Electrode will not overheat and has exceptional good mechanical properties. Can also be used as a bonding layer on dirty or oily cast iron.
Weld metal composition :Ni, Fe, Mn, C, Si |
Rm (Mpa) : 550
Re (Mpa) : 350
A5 (%) : 15
Hardness : 200—220 HB |
2.5
3.2 |
| 715 |
Special iron based electrode for repair welding of poor quality, slag or oil containing old cast iron ( furnace part, boxes, heaters, pumps,…
Also used for hard facing of cast iron press tools and dies (automotive) |
Hardness : ~ 350 HB |
3.2 |
PRODUCTS FOR HIGH TEMPERATURE & SPECIAL APPLICATIONS
| Product GOLD |
Description |
Technical details |
Size (mm) |
| 510 |
High recovery (170%) nickel base maintenance electrode.
The highly corrosion and heat resistant deposit combined with excellent mechanical properties makes this electrode a trouble shouter for many problems.
Welding of dissimilar joints, difficult to weld steels |
Rm (Mpa) : 790
Re (Mpa) : 470
A5 (%) : 35
Hardness ~ 240, 450 HB
After work hardened
Temperature Resistance > 1000°C |
2.5
3.2 |
| 520 |
Universal high nickel maintenance electrode for welding nickel alloys, dissimilar steels, high temperature steel, (Incoloy 800)cryogenic stainless steels tool steels etc.
520 is the most versatile electrodes for all difficult weld repairs. |
Rm (Mpa) : 680
Re (Mpa) : 420
A5 (%) : 40
Hardness ~ 220, 240 HB
Temperature Resistance > 1200°C |
2.5
3.2 |
| |
NON FERROUS ALLOYS |
|
|
| 610 |
ELECTRODE FOR ALUMINUM
Use for repairs and joining of Al Plates, sheets. pipes, extrusions etc.
Applications include al. engine blocks, cylinder heads ,boats construction,housings, pumps, tanks, moulds, frames, truck bodies, bus bars etc. |
Rm (Mpa) : 180
Re (Mpa) : 80
A5 (%) : 6
Weld metal composition
AL + Si |
3.2 |
| 620 |
Maintenance electrode with a complex Cu-bronze deposit for joining and surfacing of copper-alloys, steel and cast iron also for dissimilar joints between copper alloys and steels.
The deposit is corrosion, seawater and cavitations resistant with a low coefficient of friction. |
Rm (Mpa) : 660
Re (Mpa) : 420
A5 (%) : 22
Hardness ~200HB
Weld metal composition
AL + Si |
3.2 |
| 907 |
Electrode for welding copper tin bronzes and brass.
Weld deposit is resistant to salt water corrosion and therefore ideal for use in seawater desalination, naval construction, chemical and petrochemical industry |
Rm (MPa) 300
Rp (MPa) 120
A5 ( %) 20
Hardness 110 HB |
3.2 |
| 913 |
Electrode for welding copper nickel alloys with up to 30% Nickel and for final layer on Cu Ni 70/30 clad steel.
Exceptional high resistance to seawater, therefore ideal for applications in shipbuilding and repair desalination plants Oil refineries and chemical plants |
Rm (MPa) 380
Rp (MPa) 240
A5 ( %) 30
Hardness 100 HB |
3.2 |
Continue on Next Page >>
|
|